4.7 Article

Terphenyl pyridine based polymers for superior conductivity and excellent chemical stability of high temperature proton exchange membranes

期刊

EUROPEAN POLYMER JOURNAL
卷 173, 期 -, 页码 -

出版社

PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.eurpolymj.2022.111295

关键词

Poly(terphenyl pyridine); High temperature proton exchange membrane; Mechanical properties; Proton conductivity; Chemical stability

资金

  1. Joint Research Fund Liaoning She-nyang National Laboratory for Materials Science [2019JH3/30100023]
  2. National Natural Science Foundation of China [51572044]

向作者/读者索取更多资源

The novel poly(terphenyl pyridine) polymers synthesized through an acid-catalyzed polycondensation reaction exhibit high proton conductivity when doped with phosphoric acid. The membranes show good performance and stability in various tests.
A series of novel poly(terphenyl pyridine) polymers are synthesized from 4-acetylpyridine, p-terphenyl, and comonomer 2,2,2-trifluoroacetophenone via the acid-catalyzed polycondensation reaction. After doped with phosphoric acid (PA), the prepared membranes exhibit proton conductivity as high as 0.142 S cm-1 at 160 degrees C under anhydrous condition. This membrane-based single fuel cell show a peak power density of 395 mW cm-2 at 180 degrees C by fueling with non-humidified H2 and O2. A reasonable tensile stress at break of about 10 MPa is reached by the acid doped membranes under ambient atmosphere. Exposed in the Fenton reagent (3 wt% H2O2, 4 ppm Fe2}) at 68 degrees C for up to 1000 h, the membrane can still maintain original strength and possess affinity to acid molecules. After suffered the Fenton test at 68 degrees C for 200 h, the membrane is doped with PA to prepare membrane electrode assembly, which endows the single fuel cell with a power density of 206 mW cm-2 at 180 degrees C feeding with non-humidified H2 and O2.