Effect of radiation defects on the early stages of nanoindentation tests in bcc Fe and Fe-Cr alloys

期刊

COMPUTATIONAL MATERIALS SCIENCE
卷 204, 期 -, 页码 -

出版社

ELSEVIER
DOI: 10.1016/j.commatsci.2021.111151

关键词

Nanoindentation; Molecular dynamics; Radiation defects; Dislocation loops; Voids; Precipitates; Fe-based alloys; FeCr alloys; bcc Fe; Dislocations; Hardness; Reduced modulus; Ferritic-martensitic steels

资金

  1. Euratom research and training programme [755039]
  2. FOD for fusion RD
  3. CINECA award under the ISCRA initiative

向作者/读者索取更多资源

Classical molecular dynamics simulations were performed to evaluate the effect of various defects on the material response during nanoindentation tests. The presence of radiation defects did not induce significant changes in the material response, but distinct features were observed in crystals with radiation defects.
Classical molecular dynamics (MD) simulations of nanoindentation tests are performed in defect-free at 300, 600 and 1000 K and defected crystals at 300 and 600 K of pure Fe and Fe-9Cr alloy. The aim of the work is to evaluate the effect of the presence of various defects specific to neutron/heavy ion irradiation (i.e., voids, dislocation loops and Cr precipitates) on the material response during the early stages of nanoindentation (i.e., at indentation depths up to 20 angstrom). We establish that even a relatively large density of the radiation defects (similar to 10(24) m(-3)) does not induce any significant change in the material response, i.e., it is not unambiguously detectable at the force-depth curves neither in pure Fe nor in Fe-9Cr alloys. The macroscopic parameters, which can be derived from these curves, such as hardness and reduced modulus, calculated in the crystals with and without radiation defects also cannot clearly reveal the contribution from the presence of the radiation defects given the resulting uncertainty of their extraction. However, several distinct features typical for nanoindentation tests observed in crystals with radiation defects only were identified, such as a) obstruction of emission of dislocation loops under the indenter during loading for crystals with precipitates and dislocation loops, and b) special residual imprint pattern for crystals with dislocation loops. The results of this work provide useful data for the parameterization and validation of the higher-scale methods, such as dislocation dynamics and (crystal plasticity-) finite-element method. The details of the transferability of MD results to these methods are also discussed.