A lamellate composite CN/MgAl0.80Ce0.20-LDH, consisting of graphitic carbon nitride (CN) and Ce-doped MgAl-layered double hydroxide (LDH), was synthesized using a facile one-step solvothermal method. The composite showed a large specific surface area and high separation efficiency of photogenerated charge. It exhibited enhanced efficiency in removing organic dye Congo red (CR) attributed to the synergetic performance of adsorption and photocatalysis. The composite could adsorb about 49% of CR and achieve a CR degradation efficiency exceeding 90% within 180 minutes under LED visible light irradiation.
Adopting a facile one-step solvothermal method, CN/MgAl0.80Ce0.20-LDH, a lamellate composite of graphitic carbon nitride (g-C3N4, CN) and Ce-doped MgAl-layered double hydroxide (LDH), was synthesized. Profiting from the combined effect of Ce-doping and CN-LDH composition, CN/MgAl0.80Ce0.20-LDH possesses large specific surface area (52.71 m(2) g(-1)) and high separation efficiency of photogenerated charge. When used to remove organic dye Congo red (CR), the composite exhibits enhanced efficiency which can be attributed to the synergetic performance of adsorption and photocatalysis. As a result, similar to 49% CR (50 mg L-1) can be adsorbed by CN/ MgAl0.80Ce0.20-LDH and the CR degradation efficiency exceeds 90% within 180 min under light-emitting diode (LED) visible light irradiation, which is much higher than that of pristine CN (48.77%). The augmented surface area and proliferated active sites benefit the increase of adsorption capacity. The enhanced photocatalytic performance can be attributed to the efficient transmission of photogenerated electrons and holes between CN and MgAl0.80Ce0.20-LDH. Electrochemical impedance spectroscopy (EIS) analysis and photoluminescence (PL) analyses confirmed the effective separation of photogenerated electron-hole pairs in CN/MgAl0.80Ce0.20-LDH, while electron spin resonance (ESR) results verified the derivation of superoxide radicals (center dot O-2(-)) species amid CR photocatalytic degradation.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据