Process optimization and comprehensive utilization of recyclable deep eutectic solvent for the production of ramie cellulose fibers

期刊

CELLULOSE
卷 29, 期 7, 页码 3689-3701

出版社

SPRINGER
DOI: 10.1007/s10570-022-04501-0

关键词

Ramie cellulose fibers; Deep eutectic solvent; Recyclable degumming; Optimization experiment

资金

  1. National Natural Science Foundation of China [52073051, 51925302, 51873030]
  2. National Key R&D Program of China [2018YFC2000900]
  3. International Cooperation Fund of Science and Technology Commission of Shanghai Municipality [21130750100]
  4. Shanghai Committee of Science and Technology [19QA1400100]

向作者/读者索取更多资源

Deep eutectic solvents (DESs) are emerging green chemical reagents that are non-toxic, biodegradable, environmentally friendly, and easy to access. This study investigated the optimal extraction conditions and solvent recovery for DESs constituted of choline chloride and urea used in the extraction of ramie cellulose fibers. The results showed that reusable degumming solution could effectively remove non-cellulosic components even after multiple reuse, fulfilling the requirements for spinning process.
Deep eutectic solvents (DESs) are emerging green chemical reagents, most of which are non-toxic, biodegradable, environmentally friendly, and easy to access. DESs constituted of choline chloride and urea has been proved to be an innovative method for ramie cellulose fibers extraction. However, the costly DESs reagent and inefficient solvent recovery are still challenging for wide application. Here, the optimal extraction conditions and the possibility of DESs solvent recovery were investigated. Specifically, the effect of incremental reuse times of degumming solution on surface morphology, chemical composition, cellulose crystallinity (65.69 similar to 70.11%), thermal stability (thermal decomposition temperature 353 similar to 356 degrees C), degree of polymerization (1679 similar to 2445), and mechanical tenacity of degummed fibers were systematically evaluated. The results showed that reusable degumming solution could still remove the majority of non-cellulosic components from raw ramie, even after four times repeating degumming. The treated fibers achieved the cellulose content of above 90.21%, fiber yield of 74.16 similar to 78.55%, density of 6.30 similar to 7.87 dtex, tenacity of 5.21 similar to 6.72 cN/dtex, respectively. All these mechanical properties fulfilled the requirement of spinning process. Moreover, the insoluble lignin and polysaccharides were successfully separated from degumming solution and the DESs solvent was recycled with ease, beneficially realizing recycle economy and sustainable development for natural fiber extraction.