ISIJ INTERNATIONAL
卷 56, 期 12, 页码 2147-2155出版社
IRON STEEL INST JAPAN KEIDANREN KAIKAN
DOI: 10.2355/isijinternational.ISIJINT-2016-337
关键词
thermogravimetric analysis; chromite; carbothermic reduction; kinetics
资金
- Hugo Carlssons Foundation
- CAMM, Centre of Advanced Mining and Metallurgy at Lulea University of Technology
Carbothermic reduction of chromite is an important industrial process for extracting chromium from the chromite. To have a better understanding of the effect of iron on the carbothermic reduction of chromite, the reduction of synthetic chromite (FeCr2O4) by graphite with/without the addition of iron powder was investigated in this paper by Thermogravimetric Analysis (TGA) in argon atmosphere. The fractional reduced samples were examined by SEM/EDS and XRD analysis, and the reduction process was thermodynamically and kinetically evaluated. The experimental results show that the iron powder addition enhances the reduction of FeCr2O4 and this effect increases when increased amounts of iron powder are added. This phenomenon is attributed to the in situ dissolution of chromium into the iron and mixed carbide (Cr,Fe)(7)C-3, which can decrease the activity of the nascent chromium formed by the reduction of the FeCr2O4. The experimental results indicate that the reduction of FeCr2O4 with up to 80 wt.% iron powder addition is likely to be a single-step process and the kinetic analysis suggests that the reduction reaction is likely to be either (a) chemical reaction at the surface of FeCr2O4 or (b) diffusional dissolution of the product (FeCr2) into the iron/alloy particles or the mixed control of (a) and (b).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据