期刊
EMISSION CONTROL SCIENCE AND TECHNOLOGY
卷 7, 期 4, 页码 287-301出版社
SPRINGERNATURE
DOI: 10.1007/s40825-021-00201-6
关键词
Soot oxidation kinetic; Diesel particulate filter; Acicular mullite membrane filter; Aluminium fluoride; Vanadium oxide
资金
- Thailand Research Fund [RRi-PHD57I0027]
Aluminium oxide and silicon dioxide are used as raw materials for fabricating main structures of mullite diesel particulate filters, with additional substances such as titanium dioxide, aluminium fluoride, and vanadium oxide applied to develop acicular mullite structure. Carbon black is used to create pores in the filters and control factors including pore size, porosity, surface roughness, and microstructure by adjusting the amounts of additives. Raman spectroscopy analysis demonstrates that carbon black's micro and nanostructure can effectively simulate diesel soot particles, while the oxidation kinetics of soot particles on mullite and acicular mullite membrane were investigated using different techniques.
In current research, aluminium oxide and silicon dioxide are used as raw materials for fabricating main structures of mullite diesel particulate filters. The variable substances applied to develop acicular mullite structure are titanium dioxide, aluminium fluoride, and vanadium oxide. Carbon black was used to create pores in mullite diesel particulate filters with 35 to 45% porosity based on the sintering temperature of 1300 degrees C. The images of the filter's porous surface microstructure were investigated using scanning electron microscopy. Vanadium oxide and aluminium fluoride play important roles in growth of acicular shape and acicular size for membrane, respectively. Acicular size of membrane varies from a hundred nano-meters to the submicron in needle diameter. The relation of all factors between pore size, porosity, surface roughness, and pin-shape microstructure can be controlled by additional amounts of additives. From Raman spectroscopy analysis, the soot formation of carbon black's micro and nanostructure are acceptable to simulate diesel soot particles. In line with these results, carbon black was successfully used as a substitute of real engine soot in soot kinetics reactivity. In addition, the oxidation kinetics of soot particles on mullite and acicular mullite membrane were investigated by using tight contact in isothermal and loose contact in non-isothermal thermo-gravimetric analysis. The calculated apparent activation energies of soot oxidation with isothermal technique on mullite and acicular mullite membrane are approximately 213 and 141 kJ/mol while those values calculated with non-isothermal technique are 118 and 76 kJ/mol, respectively.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据