期刊
INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS
卷 54, 期 -, 页码 230-236出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ijrmhm.2015.07.026
关键词
In situ sintering reaction; Lanthanum hexaluminates; Microstructure; Mechanical properties; Origin of fracture
Al2O3-LaAl11O18-ZrO2 composites were prepared by in situ sintering reaction of different proportions of Al2O3 and La2Zr2O7. The studied batches were uniaxially pressed and pressureless sintered at 1600 degrees C up to 1725 degrees C for 1 h. Phase composition study reveals that the only present phases are alumina, lanthanum hexaluminates and zirconia. No other intermediate phases are present. Rodlike LaAl11O18 was observed in the sintered bodies containing more than 25 wt.% LaAl11O18. The effect of rodlike particles on the densification and mechanical behavior was discussed. It was found that increasing the LaAl11O18 content more than 25 wt.% enhances the fracture toughness, but reduces both the bending strength and the hardness of the sintered composites. (C) 2015 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据