INTERNATIONAL JOURNAL OF FATIGUE
卷 89, 期 -, 页码 108-118出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ijfatigue.2015.11.029
关键词
Very-high-cycle fatigue; Fatigue crack initiation; Fine-granular-area; Nanograins; High-strength steels
For high-strength steels, the crack initiation of very-high-cycle fatigue (VHCF) is commonly at the interior of material with fish-eye (FiE) morphology containing a fine-granular-area (FGA) surrounding an inclusion as crack origin, and FGA is regarded as the characteristic region of crack initiation. Here, we carefully examined the micro-morphology of FGA and FiE for two high-strength steels. The results revealed that the microscopic nature of FGA is a thin layer of nanograins. Then we proposed the formation mechanism of FGA: Numerous Cyclic Pressing (NCP) between originated crack surfaces, which causes grain refinement at originated crack wake and therefore the formation of FGA. The results of second set experiment showed that the cases with negative stress ratios exhibit the prevalence of nanograin layer in FGA region and the nanograin layer vanishes for the cases with positive stress ratios, which is a verification of the proposed NCP model. (C) 2015 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据