DOI: 10.3390/pr9122176
关键词
hydrothermal; FexCo3-xO4; electrochemical; cyclic voltammetry; the specific capacitance; HER; OER
资金
- University of Memphis, Memphis, TN, USA
- Polymer Chemistry Initiative at Pittsburg State University, Pittsburg, KS
Hydrothermally produced Fe-doped Co3O4 nanostructured particles were studied as electrocatalysts for water-splitting and electrode materials for supercapacitor devices. The addition of Fe3+ influenced the surface area, specific capacitance, and electrochemical performance of Co3O4. Fe-doped Co3O4 showed enhanced conductivity at the electrode-electrolyte interface, impacting its high activity as an electrode material.
In this study, hydrothermally produced Fe-doped Co3O4 nanostructured particles are investigated as electrocatalysts for the water-splitting process and electrode materials for supercapacitor devices. The results of the experiments demonstrated that the surface area, specific capacitance, and electrochemical performance of Co3O4 are all influenced by Fe3+ content. The FexCo3-xO4 with x = 1 sample exhibits a higher BET surface (87.45 m(2)/g) than that of the pristine Co3O4 (59.4 m(2)/g). Electrochemical measurements of the electrode carried out in 3 M KOH reveal a high specific capacitance of 153 F/g at a current density of 1 A/g for x = 0.6 and 684 F/g at a 2 mV/s scan rate for x = 1.0 samples. In terms of electrocatalytic performance, the electrode (x = 1.0) displayed a low overpotential of 266 mV (at a current density of 10 mA/cm(2)) along with 52 mV/dec Tafel slopes in the oxygen evolution reaction. Additionally, the overpotential of 132 mV (at a current density of 10 mA/cm(2)) and 109 mV with 52 mV/dec Tafel slope were obtained for x = 0.6 sample towards hydrogen evolution reaction (HER). According to electrochemical impedance spectroscopy (EIS) measurements and the density functional theory (DFT) study, the addition of Fe3+ increased the conductivity at the electrode-electrolyte interface, which substantially impacted the high activity of the iron-doped cobalt oxide. The electrochemical results revealed that the mesoporous Fe-doped Co3O4 nanostructure could be used as potential electrode material in the high-performance electrochemical capacitor and water-splitting catalysts.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据