In the present work, Ni-based filler metal was used to weld a new type of 10% Cr martensitic steel. Due to the microstructure and chemical composition difference between martensitic steel and the Ni-based weld metal, a clear interface existed in the dissimilar welded joint. At the region of the interface, the microstructure was physically connected and an element transition layer was formed. Low-cycle fatigue (LCF) results showed that the welded joint was not fractured at the interface. Meanwhile, the martensitic steel and Ni-based weld metal exhibited cyclic softening and cyclic hardening behaviors, respectively. For martensitic steel, the width of the laths increased and the dislocation density decreased after the fatigue test, whereas in the fatigue-tested Ni-based weld metal, the dislocation density increased. The continuous connection and composition transition at the region of interface, combined with the high ductility and cyclic hardening behavior of Ni-based weld metal, is beneficial for the LCF properties of the welded joint. (C) 2016 Published by Elsevier Ltd.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据