DOI: 10.1007/s40843-021-1785-6
关键词
broadband near-infrared; double-perovskite; Sr2ScSbO6:Cr3+; pc-LEDs; solar-like spectrum
资金
- National Natural Science Foundation of China [51972020, 51832005]
A new broadband NIR phosphor Sr2ScSbO6:Cr3+ has been developed, showing high luminescence efficiency and thermal stability for potential use in solar-like lighting applications.
For healthy lighting, daily lighting that considers both visible light and near-infrared (NIR) light is necessary. However, at similar to 900 nm, the extensively used solar-like phosphor-converted light-emitting diodes (pc-LEDs) are limited by a lack of high-performance NIR luminescent materials. We report a broadband NIR phosphor Sr2ScSbO6:Cr3+ with a double perovskite-type structure, thus simultaneously demonstrating high luminescence efficiency and good thermal stability. Under 550-nm excitation, Sr2ScSbO6:Cr3+ demonstrates broadband NIR emission centered at similar to 890 nm with luminescence internal/external efficiencies of 82.0%/35.7%, respectively. Furthermore, the luminescence integrated intensity at 430 K remains at similar to 66.4% of the initial intensity. We successfully fabricated pc-LED devices using a 465-nm-sized blue chip and other commercial phosphors, presenting a relatively complete solar-like spectrum from blue to NIR light and is expected to be used in solar-like lighting.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据