Complex Structure Modification and Improvement of Properties of Aluminium Casting Alloys with Various Silicon Content

The possibility of using complex structure modification for aluminium casting alloys' mechanical properties improvement was studied. The fluxes widely used in the industry are mainly intended for the modification of a single structural component of Al-Si alloys, which does not allow unifying of the modification process in a production environment. Thus, a new modifying flux that has a complex effect on the structure of Al-Si alloys has been developed. It consists of the following components: TiO2, containing a primary alpha-Al grain size modifier; BaF2 containing a eutectic silicon modifier; KF used to transform titanium and barium into the melt. The effect of the complex titanium dioxide-based modifier on the macro-, microstructure and the mechanical properties of industrial aluminium-silicon casting alloys containing 5%, 6%, 9%, 11% and 17% Si by weight was studied. It was found that the tensile strength (sigma(B)) of Al-Si alloys exceeds the similar characteristics for the alloys modified using the standard sodium-containing flux to 32%, and the relative elongation (delta) increases to 54%. The alloys' mechanical properties improvement was shown to be the result of the flux component's complex effect on the macro- and microstructure. The effect includes the simultaneous reduction in secondary dendritic arm spacing due to titanium, the refinement and decreasing size of silicon particles in the eutectic with barium and potassium, and the modifying of the primary silicon. The reliability of the studies was confirmed using up-to-date test systems, a significant amount of experimental data and the repeatability of the results for a large number of samples in the identical initial state.

Automated summary

The study explores the use of complex structure modification to improve the mechanical properties of aluminium casting alloys, and a new modifying flux with complex effects on the structure of Al-Si alloys has been developed. The research found that the modifying flux had a significant impact on the macro- and microstructure of the alloys, resulting in improved tensile strength and elongation properties.