Facile Synthesis of Solubilizing a Group-Free, Solution-Processable p-Type Ladder Conjugated Polymer and Its Thermoelectric Properties

Here we report the synthesis of a new solubilizing group-free, solution-processable p-type ladder conjugated polymer, 6H-pyrrolo[3,2-b:4,5-b']bis[1,4]benzothiazine ladder (PBBTL) pol-ymer by using a polyphosphoric acid (PPA) and phenylphosphonic acid (PhPO3H2) 1:1 binary acid solvent system together with careful control of reaction kinetics. With a good intrinsic viscosity of 3.69 dL/g in methanesulfonic acid (MSA), good quality PBBTL films can be obtained via spin-coating. Intrinsic thin film properties and thermoelectric performance of PBBTL were evaluated, making it the second solubilizing group-free, solution-processable ladder-type conjugated polymer after BBL to be used for thin-film polymer electronics. While our preliminary thermoelectric performance of the FeCl3-doped PBBTL films is modest, we believe that many opportunities lie ahead for PBBTL and hope that its successful synthesis using the new PPA:PhPO3H2 binary acid solvent system will inspire synthetic organic chemists to relook into solubilizing group-free, solution-processable ladder-type conjugated polymer systems.

Automated summary

The synthesis of a new solubilizing group-free, solution-processable ladder conjugated polymer PBBTL was reported, with its thin film properties and thermoelectric performance evaluated. Despite modest initial results, there are opportunities for further development and exploration in this field.