Study on the effect of size on InGaN red micro-LEDs

In this research, five sizes (100 x 100, 75 x 75, 50 x 50, 25 x 25, 10 x 10 mu m(2)) of InGaN red micro-light emitting diode (LED) dies are produced using laser-based direct writing and maskless technology. It is observed that with increasing injection current, the smaller the size of the micro-LED, the more obvious the blue shift of the emission wavelength. When the injection current is increased from 0.1 to 1 mA, the emission wavelength of the 10 x 10 mu m(2) micro-LED is shifted from 617.15 to 576.87 nm. The obvious blue shift is attributed to the stress release and high current density injection. Moreover, the output power density is very similar for smaller chip micro-LEDs at the same injection current density. This behavior is different from AlGaInP micro-LEDs. The sidewall defect is more easily repaired by passivation, which is similar to the behavior of blue micro-LEDs. The results indicate that the red InGaN epilayer structure provides an opportunity to realize the full color LEDs fabricated by GaN-based LEDs.

Automated summary

In this research, it is observed that the smaller the size of the InGaN red micro-LED, the more obvious the blue shift of the emission wavelength with increasing injection current. Smaller chip micro-LEDs exhibit similar output power density at the same injection current density.