High-entropy alloys; Powder metallurgy; Mechanical alloying and milling; Microstructure; Mechanical properties
资金
- State Key Laboratory of Powder Metallurgy Central South University, Changsha, China
- Project of Innovation-driven Plan in Central South University [2015CX004]
In this work, nanocrystalline CrMnFeCoNi HEAs were prepared by powder metallurgy. It was found mechanical milling can further refine the microstructures and morphologies of the gas-atomized powder, and increase the sintering ability. The HEAs sintered from the mechanically milled powder have much finer microstructures than that from the gas-atomized powder. The original morphology and defects in both the gas-atomized and the mechanically milled powders can be inherited to the bulk forms after the SPS. The SPSed HEAs have a tensile strength as high as 1000 MPa at room temperature and reasonable ductility. The strengthening mechanism can be attributed to the nanocrystalline microstructures, in which grain boundaries block the movement of dislocations. Powder metallurgy can be taken as a promising way for preparing HEAs with high mechanical properties. (C) 2015 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据