Martensitic steel; Corrosion; Electrochemical impedance spectroscopy; Slow strain rate test; Molten salt
资金
- CONICYT/FONDAP - Antofagasta Government [15110019, FIC-R 30413089-30488809]
- Fondecyt [11200388]
In the field of Concentrated Solar Power (CSP), the choice of metallic materials for critical components is crucial and evolving towards superior performance and cost competitiveness. Research on the corrosion behavior and mechanical properties of martensitic steel in promising ternary molten salts has revealed that the steel is more ductile but less robust in high-temperature molten salt environments.
In the context of Concentrated Solar Power (CSP), the metallic materials employed to build the critical components of the plant are exposed to severe conditions, Carbon and stainless steel have been used for this application. However, the technology CSP will evolve, so these materials will probably be replaced by superior performing and economically competitive ones. Likewise, the investigation of molten salts with better thermophysical properties but no more corrosive than the actual benchmark has become a complex challenge. Thus, the research motivation was to study the performance of a martensitic steel exposed to a promising ternary molten salt with lithium nitrate at 550 degrees C by its corrosion behavior and mechanical properties. The corrosion process was monitored through electrochemical impedance spectroscopy (EIS). The mechanical properties in molten salt at high temperature were determined by slow strain rate testing (SSRT), complementing with the characterization of corrosion products to propose the corrosion mechanism in one scheme. The results showed that the steel is less robust but more ductile in the presence of molten salts at high temperatures; besides the material develop a multi-layer non-porous corrosion product that, despite deteriorating, confers corrosion rates within the recommended ranges for the application.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据