INTERMETALLICS
卷 77, 期 -, 页码 46-56出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.intermet.2016.07.001
关键词
High entropy alloy; Spark plasma sintering; Transmission electron microscopy (TEM); Phase transformation; Diffraction
资金
- DST-SERB, New Delhi [SB/FTP/ETA-181/2013]
The present paper reports synthesis of novel AlFeCuCrMgx (x = 0, 0.5, 1, 1.7 mol) high entropy alloys (HEAs) by mechanical alloying (MA) followed by spark plasma sintering (SPS). Phase evolution, microstructure and phase transformation study of the sintered alloy were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and differential scanning calorimetry (DSC). XRD of the sintered alloys revealed the formation of two BCC phases in the AlFeCuCr alloy and more complex structures in AlFeCuCrMgx (x = 0.5, 1, 1.7) alloys containing AlFe type, BCC, and Cu2Mg type phases. TEM bright field image and selected area diffraction pattern (SAED) revealed the formation of tetragonal closed packed Cr precipitates within the Cu2Mg phase of AlFeCuCrMgx alloys (x = 0.5, 1, 1.7). DSC study of the alloys revealed no substantial phase change up to 1000 degrees C for AlFeCuCr alloy. Although, for x = 0.5, 1 & 1.7 phase transformation occurs at 818 degrees C, 885 degrees C & 483 degrees C respectively. Mg content had a significant effect on hardness, increasing to a peak hardness of 853 HVN for AlFeCuCrMg0.5 alloy before decreasing to 533 HVN for the AlFeCuCrMg1.7 alloy. The phase evolution in these alloys has been considered using thermodynamic parameters, and the structure-property relationship has also been proposed by conventional strengthening mechanisms. Crown Copyright (C) 2016 Published by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据