brewers' spent grain; poly(epsilon-caprolactone); wood-polymer composites; filler modification; aging resistance
资金
- National Science Centre (NCN, Poland) [2018/28/C/ST8/00187]
This paper investigated the effects of brewers' spent grain (BSG) extrusion parameters on the photo-oxidative resistance of poly(epsilon-caprolactone)-based wood polymer composites. Filler samples with higher melanoidin content were more effective in hindering polymer degradation and inhibiting the decomposition of the polymer amorphous phase. Therefore, deterioration of mechanical performance was limited, as indicated by higher aging factor values for samples containing BSG extruded at higher temperatures.
The presented paper investigated the influence of brewers' spent grain (BSG) extrusion parameters on the photo-oxidative resistance of poly(epsilon-caprolactone)-based wood polymer composites. Filler samples characterized by the higher melanoidin content were more efficient in hindering of polymer degradation, inhibiting the decomposition of the polymer amorphous phase. As a result, deterioration of mechanical performance was limited, which was expressed by the higher values of aging factor for samples containing BSG extruded at higher temperatures.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据