期刊
INFRARED PHYSICS & TECHNOLOGY
卷 76, 期 -, 页码 580-586出版社
ELSEVIER
DOI: 10.1016/j.infrared.2016.04.022
关键词
AZO substrate; IR transmittance; Thermochromics; Vanadium dioxide film
A vanadium dioxide (VO2) thin film was fabricated on a ZnO doped with Al (AZO) conductive glass by magnetron sputtering at room temperature followed by annealing under air atmosphere. The microstructures and optical properties of the thin film were studied. The results showed that the VO2/AZO composite film was poly-crystalline and the AZO layer did not change the preferred growth orientation of VO2. Compared to the VO2 film fabricated on soda-lime glass substrate through the same process and condition, the phase transition temperature of the VO2/AZO composite film was decreased by about 25 degrees C, thermal hysteresis width narrowed to 6 degrees C, the visible light transmittance was over 50%, the infrared transmittances before and after phase transition were 21% and 55%, respectively at 1500 nm. (C) 2016 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据