DOI: 10.1016/j.msea.2022.142863
关键词
2219-T8 aluminum alloy; Partially melted zone (PMZ); TIG welding; Tensile properties; Stress distribution
类别
资金
- National Natural Science Foundation of China [U1637601]
The tensile properties of 2219-T8 aluminum alloy TIG welding joints were improved by enhancing the local properties of the partially melted zone (PMZ) and adjusting the stress distribution at the weld toe. Refining the grain size and controlling the theta phase particles in the base metal effectively increased the tensile strength and elongation of the PMZ.
Tensile properties of 2219-T8 aluminum alloy TIG welding joints were seriously restricted by partially melted zone (PMZ) properties and stress concentration at weld toe. In this work, PMZ local properties were enhanced by refining grains size and theta phase particles in base metal. And the stress concentration at weld toe was adjusted using three-pass welding with swing. The results showed that tensile strength of PMZ was increased by -16-21 MPa, due to the higher Cu content of matrix, as well as reduced coarse and continuous eutectic. The joint tensile strength of -318 MPa (-10% increase) and elongation of -5.8% (-26% increase) were obtained by improving PMZ local properties and matching proper stress distribution.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据