elective laser melting; Titanium alloys; Microstructure; Mechanical properties
类别
资金
- National Natural Science Foundation of China [51975061, 51775055]
- Natural Science Foundation of Hunan Province [2020JJ5599]
- Research Foundation of Education Bureau of Hunan Province [19C0032, 19B033]
The study systematically investigated the SLM of Ti-15Mo alloy, particularly focusing on densification, microstructure, and mechanical properties. The samples processed by SLM exhibit a greater combination of high tensile strength and elongation due to the retention of omega phase, high dislocation density, finer grains, twinning-induced plasticity, and changes in texture orientation.
In this study, selective laser melting (SLM) of Ti-15Mo alloy was systematically investigated, especially in its densification, microstructure and mechanical properties. At low scanning speed, the formation of spherical holes are mainly due to gas porosity brought about by residual gases. At high scanning speed, the lack of fusion (LOF) defects are presented because of the insufficient energy density, which is very detrimental to the ductility. Owing to the difference of the temperature gradient, the transition from the cellular crystals to equiaxed crystals has been observed in XY plane while the XZ plane are mainly consist of columnar crystals which are radiating along the edge of the molten pool. As a result of the retention of a reasonable level of omega phase, high dislocation density, finer grains, the twinning-induced plasticity (TWIP) and the changes of texture orientation, the Ti-15Mo samples processed by the SLM achieve a greater combination of high tensile strength of 840.41 MPa and a high elongation of 32.37%, which are higher than those reported so far. The twins become denser and thicker with increasing strain, and the average of twin widths with various strains were calculated to 7 mu m at strain of 10%, 4 mu m at strain of 15% and 2 mu m at strain of 20%.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据