The introduction of Sr doping into LiFe5O8 bulk material results in an enhanced dielectric constant and reduced dielectric loss. The Sr-doped samples exhibit relaxation behavior suitable for high frequency applications. Temperature and frequency dependent measurements show promising results for practical use.
We report on enhanced dielectric constant and reduction in dielectric loss with Sr doping in LiFe5O8 bulk material. LiSrxFe5-xO8 (x = 0, 0.025, 0.05) samples are seen to crystallize in ordered alpha- LiFe5O8 phase. Dielectric constant is observed to increase from 2 x 104 to 3 x 106 and loss decreases with the doping of Sr at Fe site. Temperature dependent DC conductivity follows the Arrhenius relationship and the activation energy associated with the conduction process is seen to be 0.42, 0.41 and 0.52 eV for the LiSrxFe5-xO8 (x = 0, 0.025, 0.05) samples. Temperature and wide frequency dependent dielectric measurements indicate that the Sr doped LiFe5O8 samples exhibit relaxation behavior and can be employed for high frequency applications.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据