This paper investigates the in-plane shear response of a flax fiber - epoxy resin composite laminate, revealing the presence of stress concentrators in the specimen at high stress levels. Additionally, the material stiffens approximately 9% with increasing loading speed, indicating the presence of a viscoelastic component during loading.
The present paper is aimed at studying the in-plane shear response of a flax fiber - epoxy resin composite laminate. Rectangular specimens, with +/- 45 degrees laminate orientation with respect to loading direction were used for the experimental procedure. Tensile testing up to failure allowed to extract the shear strain-shear stress curve, which have shown a linear domain, up to approximately 25 MPa, where a shear modulus was calculated, of 1.67 GPa and a Poisson ratio of 0.7, value which is typical for off axis laminates. Strain measurement during these tests, using Digital Image Correlation, have shown that, at high stress levels, concentrators occur in the specimen in the region of failure. Repeated loading tests have shown that the material stiffens approximately 9% when increasing loading speed, leading to conclude that a viscoelastic component of the deformation is present during loading. Repeated creeprecovery tests showed that, for longer periods of time, viscoplastic deformations appear as well, with an exponential evolution with respect to the creep duration.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据