The present study focuses on the synthesis, structure, and luminescent properties of Zn4Al22O37 phosphors doped with cerium (Ce3+) and europium (Eu3+). The phosphors were prepared using a solution combustion synthesis route and their structural properties were examined using various techniques. The luminescence properties were characterized using different excitation wavelengths and the Commission Internationale de l'Eclairage (CIE) color coordinates were determined. The results suggest that these phosphors show potential for use in lighting applications.
The present communication is strongly focused on the investigation of synthesis, structural and luminescence properties of cerium (Ce3+)- and europium (Eu3+)-activated Zn4Al22O37 phosphors. Ce3+- and Eu3+-doped Zn4Al22O37 novel phosphors were prepared using a solution combustion synthesis route. Structural properties were studied using powder X-ray diffraction and high-resolution transverse electron microscopy. The optical properties were studied using ultraviolet-visible light spectroscopy and Fourier transform infrared spectroscopy; luminescence properties were studied using a photoluminescence (PL) technique. The crystal structure of the prepared Zn4Al22O37 host and Ce3+- and Eu3+-activated Zn4Al22O37 phosphors was investigated and was found to have a hexagonal structure. The measured PL emission spectrum of the Ce3+-doped Zn4Al22O37 phosphor showed an intense and broad emission band centred at 421 nm under a 298 nm excitation wavelength. By contrast, the Eu3+-doped Zn4Al22O37 phosphor exhibited two strong and intense emission bands at approximately 594 nm (orange) and 614 nm (red), which were monitored under 395 nm excitation. The Commission Internationale de l'Eclairage (CIE) colour coordinates of the Ce3+-doped Zn4Al22O37 were investigated and found to be x = 0.1567, y = 0.0637 (blue) at 421 nm and for Eu3+-doped Zn4Al22O37 were x = 0.6018, y = 0.3976 (orange) at 594 nm and x = 0.6779, y = 0.3219 (red) at 614 nm emission. The luminescence behaviour of the synthesized phosphors suggested that these phosphors may be used in lighting applications.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据