Cold sintering of the ceramic potassium sodium niobate, (K0.5Na0.5)NbO3, and influences on piezoelectric properties

Cold Sintering was applied to densify a Potassium-Sodium Niobate solid solution composition, 0.5KNbO(3)-0.5NaNbO(3) (KNN); the process uses a transient chemical sintering aid, moderate pressure (400 MPa), and temperatures between 230-300 degrees C to obtain ceramics of Psi similar to 92 to 96 % theoretical density. Typically, sintering temperatures between similar to 1000-1050 degrees C are required to density KNN using conventional methods. In this paper, the densification was investigated during heating, particularly the shrinkage in the first 60 min of the cold sintering process. The low-field dielectric and electrical properties of the resulting ceramics were found to be comparable to conventionally sintered KNN. Electric fields up to 80 kV/cm could be applied, however the ceramics showed pinched hysteresis loops, even after poling over a wide range of temperatures and electric fields. A Rayleigh analysis was used to investigate domain dynamics and high reversible permittivity. The irreversible behavior was an order of magnitude lower than in conventionally sintered KNN, likely associated with defect pinning of ferroelectric domains. A Transmission Electron Microscopy (TEM) study revealed a high density of line defects in most grains; dislocations in the grains limit poling and domain wall movement, thus suppressing both the piezoelectric properties and the hysteresis. Furthermore, TEM observations indicated crystalline grain boundaries that were faceted with terrace kink ledges. These observations point to the importance of the initial powder optimization and grain boundary diffusion when using cold sintering to prepare ceramics that are intended to show bulk cooperative properties such as ferroelectricity. The impact of limited high temperature homogenization of bulk diffusional processes is discussed.

Automated summary

In this study, Cold Sintering was applied to densify a Potassium-Sodium Niobate solid solution composition, resulting in ceramics with comparable dielectric and electrical properties as conventionally sintered KNN. TEM analysis revealed high density of line defects in grains and crystalline grain boundaries with faceted kinks, which limit the piezoelectric properties and hysteresis of the ceramics.