Poly(silylene arylether arylacetylene) resin; Reaction of terminal acetylene with inner acetylene groups; Blended arylacetylene resin; Heat-resistant resin; High performance resin for advanced composite
资金
- National Natural Science Foundation of China [21805088]
- Shanghai Aerospace Science and Technology Innovation Fund [SAST2017-142]
- Fundamental Research Funds for the Central Universities [JKD012116011]
The introduction of terminal acetylene compound can increase the reaction extent of inner acetylene groups in silicon-containing arylether arylacetylene resin, leading to improved flexural strength and heat resistance of the blended resin.
Silicon-containing arylether arylacetylene resin is a kind of high-performance resins with good processabilities, mechanical properties and heat-resistance, but a shortcoming in mechanical properties at high temperatures. To address this problem, the reactions between a terminal alkyne compound and an inner alkyne compound were investigated and the results show that the terminal acetylene group could react with the inner acetylene group, which leads to the increase in the reaction extent of the inner acetylene group. The terminal alkyne compound was introduced into a silicon-containing arylether arylacetylene resin to further investigated the effect of reactions among acetylene groups. As a result, when the content of terminal acetylene group reaches about 70% in a blended resin, the reaction extent of the inner acetylene groups reaches 68.7%, and the flexural strength of the blended resin at 300 celcius raises up to 34.6 MPa and increases by 242.5% as compared with the silicon-containing arylether arylacetylene resin without the terminal alkyne compound.