Novel carbon dots as efficient green corrosion inhibitor for mild steel in HCl solution: Electrochemical, gravimetric and XPS studies

期刊

出版社

PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.jpcs.2021.110341

关键词

Carbon dots; Corrosion inhibitor; Mild steel; Acid environment

向作者/读者索取更多资源

Carbon dots (CDMU and CDMH) were synthesized and characterized as eco-friendly corrosion inhibitors for mild steel in 15% HCl solution. Both inhibitors showed high inhibition efficiency and followed Langmuir adsorption isotherm on the surface of mild steel. Various characterization techniques were used to study the inhibitive effect and adsorption behavior of CDMU and CDMH on the metal surface.
Eco-friendly, good water soluble and inexpensive, carbon dots (CDMU and CDMH) were synthesized, characterized and applied as corrosion inhibitor for mild steel (MS) in 15% HCl solution. The characterization of both inhibitors was carried out by FTIR, UV-vis, photoluminescence, XPS and TEM. The average size of CDMU and CDMH were found as 2.03 and 2.5 nm, respectively. The inhibitive effect of CDMU and CDMH was evaluated by weight loss measurement, electrochemical impedance spectroscopy and potentiodynamic polarization measurement. Both CDMU and CDMH exhibited 97.89 and 90.10% of inhibition efficiency, respectively, at 100 mg/L concentration and 303 K temperature. Adsorption of CDMU and CDMH on MS surface followed Langmuir adsorption isotherm. The surface morphology of uninhibited and inhibited MS specimens was studied by the FESEM, AFM and XPS analysis.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.5
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据