JOURNAL OF PHYSICAL CHEMISTRY C
卷 126, 期 1, 页码 611-616出版社
AMER CHEMICAL SOC
DOI: 10.1021/acs.jpcc.1c08232
关键词
-
资金
- National Natural Science Foundation of China [51572222]
- Key Research Project of the Natural Science Foundation of Shaanxi Province, China [2021JZ-08, 2020JM-088]
The coexistence of metallicity and ferroelectricity-like polarization is reported at GdAlO3/SrTiO3 heterointerfaces, where the transport property can be significantly manipulated by switching the polarization state. The switchable conductance improves under the influence of a polarization state at 6 V, accelerating the commercial application of oxide devices.
Application of multifunctional integrated devices represents a main trend in the future. However, it is still a great challenge to realize ferroelectric metals in a single system. Here, we report the coexistence of metallicity and ferroelectricity-like polarization at GdAlO3/SrTiO3 heterointerfaces. The results show that the asymmetric bistable polarization in the GdAIO 3 film is attributed to the spontaneous polarization of oxygen vacancies. Furthermore, the transport property of GdAlO3/SrTiO3 heterointerfaces can be significantly manipulated by switching the polarization state. It is observed that the switchable conductance significantly improves under the influence of a polarization state at 6 V. Its change in the resistance is about 17.2% under 10 V, which accelerates the commercial application of oxide devices.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据