期刊
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
卷 92, 期 -, 页码 88-97出版社
JOURNAL MATER SCI TECHNOL
DOI: 10.1016/j.jmst.2021.03.033
关键词
Nickel-based single crystal superalloys; Dendritic structure; Inhomogeneity; Creep; Rafting; Dislocation networks
资金
- National Natural Science Foundation of China [91960201, 51988101]
- Key Basic Research Program of Zhejiang Province [2020C01002]
- Zhejiang Provincial Natural Science Foundation of China [LY20E010004]
- Fundamental Research Funds for the Central Universities [2019QNA4012]
- Innovation Fund of the Zhejiang Kechuang New Materials Research Institute [ZKN-18-Z01]
- Centre of Electron of Microscopy of Zhejiang University
The creep inconsistency between dendrite core and interdendritic region was investigated in a nickel-based single crystal superalloy, showing that higher elemental inhomogeneity leads to local strength deviation, while increased solid solution time can reduce overall inhomogeneity and relieve creep inconsistency.
The creep inconsistency between dendrite core and interdendritic region is investigated in a nickel-based single crystal superalloy under 1373 K and 137 MPa. Two specimens with higher and lower degree of elemental inhomogeneity on dendritic structures are compared. For specimen with higher inhomogeneity, stronger segregation of refractory elements reinforces the local strength in dendrite core, but damages the strength in interdendritic region. Creep strain is accumulated faster in interdendritic region giving rise to promoted dislocation shearing in gamma' phase, faster degradation of dislocation networks and facilitated topological inversion of rated structures. Although the segregation of refractory elements produces a high density of topologically close-packed (TCP) phase in dendrite core, faster accumulation of creep strain forms microcracks prior in interdendritic region that gives rise to final rupture of the specimen. In another specimen, increased solid solution time gives rise to overall reduced inhomogeneity. Creep inconsistency is relieved to show more uniform evolution of dislocation substructures and rafting between dendrite core and interdendritic region. The second specimen is ruptured by formation and extension of microcracks along TCP phase although the precipitation of TCP phase is relatively restricted under reduced inhomogeneity. Importantly, the balance of local strength between dendrite core and interdendritic region results in over 40% increase of creep rupture life of the second specimen. (C) 2021 Published by Elsevier Ltd on behalf of Chinese Society for Metals.