In this study, Sr0.4La0.3Ca0.3Fe11.85Al1.0Co0.15O19 was used to investigate the effect of different doping amounts of Bi2O3 on its magnetic characteristics. With the increase of Bi2O3 doping, the grain size of the sample gradually increased, while the uniformity of the grain size decreased. When the Bi2O3 doping amount was 1.0 wt%, the sample showed the best performance.
Considering the improvement of electronics regarding high frequency and miniaturization, SrM hexaferrites need to exhibit high anisotropy field H-a, high remanence ratio M-r/M-s, and low ferromagnetic resonance linewidth Delta H to create microwave devices and equipment with planarisation, miniaturisation, and high frequencies. The key to achieving self-biased microwave devices with high-frequency is to simultaneously achieve high H-a, high M-r/M-s, and low Delta H. However, it is hard to meet these requirements. In this study, Sr0.4La0.3Ca0.3Fe11.85Al1.0Co0.15O19 was used to study the effect of different doping amounts of Bi2O3 on its magnetic characteristics, micromorphology and FMR linewidth. With the increase of Bi2O3 doping, the grain size of the sample gradually increased, and the uniformity of the grain size gradually decreased. When the Bi2O3 doping amount x increased from 0 to 1.2 wt%, the 4 pi M-s and 4 pi M-r values increased and the coercivity displayed the opposite tendency. The samples showed great uniaxial anisotropy. The magnetocrystalline anisotropy field H-a shows a trend of initially decreased and then increased. When x = 1.0 wt%, H-a reaches the maximum value of 28.9 kOe. At this time, the ferromagnetic resonance linewidth AH of the sample is 1578 Oe. The theory of IGA was adopted to divide the FMR linewidth into two parts Delta H-a and Delta H-p. Accroding to the results, Delta H-a takes the bigger proportion of linewidth. However, the change in Delta H-p is not negligible. When x = 1.0 wt%, the sample showed its best performance (4 pi M-s = 3412 Gs, 4 pi M-r = 2905 Gs, H-c = 2649 Oe, M-r/M-s = 85.1%, large H-a = 28.864 kOe, and Delta H = 1578 Oe). The SrM ferrite materials provided in this study can potentially be used in the microwave engineering, high-frequency, and self-biased devices.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据