Iron bismuth glasses; Thermoelectric power; Small polaron hopping
The study revealed that glasses containing iron and bismuth elements have good solubility and electrical properties, with glasses containing Sr showing particularly interesting electrical characteristics.
Glasses with nominal composition 70Bi(2)O(3)-30Fe(2)O(3) and 10X-60Bi(2)O(3)-30Fe(2)O(3) (mol%); (X = Ba, Sr and Ca) were prepared by the conventional melt quenching technique. X-ray diffraction and differential scanning calorimeter confirm the amorphous nature of the glass samples. The iron-bismuth glass shows good solubility of alkaline earth elements ions. In temperatures range of 310-450 K, the de conductivity of the glass samples containing alkaline earth elements enhanced. Glass sample containing Sr shows interesting electrical properties. All glass samples showed a transition from negative to positive Seebeck coefficient, this means that the conduction is mixed of electrons and holes charge carriers. The conduction mechanism of all samples obeys non-adiabatic small polaron hopping model of electron between iron ions. The calculated small polaron coupling constant, (gamma(p)) was found to be in the range of 10.25-17.28. Also, the calculated hopping mobility (mu) and carrier density (N-c) of glasses were in the range of 4.65 x10(-7) to 4.11 x10(-3), ( cm(2) V-1 s(-1)) and 0.029-10 (x10(17) cm (-3)) at 333 K, respectively. The conductivity of the present glasses was primarily determined by hopping carrier mobility.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据