期刊
JOURNAL OF CLEANER PRODUCTION
卷 331, 期 -, 页码 -出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.jclepro.2021.130022
关键词
Eco-friendly concrete; Artificial lightweight fine aggregate; Mineral admixtures; Durability; Sulfate attack; Wetting-drying cycle
资金
- National Natural Science Foundation of China [51922079, 61911530160]
- Natural Sci-ence Foundation of Jiangsu Province of China [BK20190604]
- Jiangsu Planned Projects for Postdoctoral Research Funds [2020Z327]
- Key Laboratory of Road and Traffic Engineering of the Ministry of Education, Tongji University [K202002]
- Key Research Project from Shanxi Transportation Holdings Group [19-JKKJ-1]
- Funds of Science and Technology Commission of Shanghai Munic-ipality [20DZ2251900]
- Jiangnan University
This study examined the durability of eco-friendly lightweight concrete (LWC) under sulfate erosion. Results showed that LWC exhibited better resistance to sulfate attack compared to conventional concrete, thanks to its internal curing and adequate cement hydration. Increasing the volume of fly ash led to worse durability. A mix of 20% fly ash, 10% metakaolin, and 10% blast furnace slag showed excellent sulfate resistance with increased flexural strength.
Sulfate erosion, as one of the most aggressive environmental attack, can cause severe damage to concrete in-frastructures. This study examined the durability of an eco-friendly lightweight concrete (LWC), made with artificial lightweight fine aggregate and various mineral admixtures exposed to both physical and chemical sulfate attack by performing the change of concrete mass, dynamic elastic modulus, flexural strength, and SEM and XRD analyses. Results show that LWC exhibits better sulfate resistance with less erosion products, i.e., ettringite and gypsum, since the internal curing of LWC contributes to adequate cement hydration that hinders the attack of sulfate ions. With an increase in fly ash volume, worse durability can be observed. A mix of 20% fly ash, 10% metakaolin and 10% blast furnace slag presents excellent sulfate resistance with an increase of 5.43% in flexural strength (even after 35 cycles of dual sulfate attack) compared to its initial 28-day strength. However, the LWC blended with 20% fly ash and 10% metakaolin shows the worst resistance with more erosion products resulting in a maximum strength loss of 23.62% given a 35-cycle attack. With the presented analysis, a theo-retical basis for the improvement of concrete durability under severe environmental attack can be provided.