TiB2 in Ti matrix; TiB whiskers; transformation kinetics; complex Avrami kinetics
资金
- European Regional Development Fund, Hungary [GINOP-2.3.2-5-2016-00027]
- European Union
The study investigated the kinetics of transformation of 5 w% TiB2 nano-particles dispersed in a Ti matrix, finding that a complex Avrami kinetics described the transformation better than the classical one-step Avrami kinetics due to the formation of oxide inhibitors from contaminants.
The kinetics of transformation of 5 w% TiB2 nano-particles (50 nm diameter) dispersed and pressed (1.5 GPa) in the of Ti matrix (150 mu m diameter) into TiB nano-whiskers was studied as a function of temperature (800-900-1000 degrees C) and time (5-720 min) in 25 experiments in total, by vacuum sintering. The classical one-step Avrami kinetics does not properly describe this transformation due to the formation of oxide inhibitors from contaminants. However, the same results could be perfectly described by a complex Avrami kinetics supposing two parallel steps of transformations: i). fast transformation along the initially metallic Ti/TiB2 interface and ii). delayed transformation along contaminated Ti/TiB2 interface. Data for kinetic calculation was obtained by X-ray diffraction and Rietveld refinement on the sintered samples. Extrapolating the experimental results by the complex Avrami model beyond the measured temperature interval it was found that at and above about 1050 degrees C, the second step is missing due to the fast dissolution of oxide films in the beta-Ti matrix, leading to very fast kinetics. (C) 2021 The Authors. Published by Elsevier B.V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据