卷 17, 期 1, 页码 22-38出版社
SPRINGER INT PUBL AG
DOI: 10.1007/s40962-022-00768-y
关键词
ductile iron; aluminum alloying; thermomechanical behavior
This study investigates the effect of aluminum alloying on the static and transient thermomechanical behavior of SiMo ductile iron. Experimental methods were used to evaluate the high-temperature capability of different alloys. The results show that aluminum alloying improves the dimensional stability and oxidation protection of the material. The optimal level of aluminum alloying depends on the thermomechanical conditions of application.
Silicon and molybdenum (SiMo) ductile iron is commonly used for exhaust manifolds because these components experience thermal cycling in oxidizing environment, which requires resistance to fatigue during transient thermomechanical loads. Previous studies have demonstrated that alloying elements, such as Al, to SiMo ductile iron reduces the amount of surface degradation during static high-temperature exposure. However, deterioration of sphericity of the graphite nodules and a decrease in ductility could affect the tendency of cracking during thermal cycling. In this article, the effect of Al alloying on static and transient thermomechanical behavior of SiMo ductile iron was investigated to optimize the amount of Al alloying. A thermodynamic approach was used to confirm the effect of the Al alloying on the phase transformations in two SiMo cast irons, alloyed by 1.8% Al and 3% Al. These two alloys were cast in a laboratory along with the baseline SiMo ductile iron. Several experimental methods were used to evaluate the dimensional stability, physical properties, static oxidation, and failure resistance during constrained thermal cycling testing to compare their high-temperature capability. Experimental results verified that Al alloying increases the temperature range and decreases volume change during eutectoid transformation, which together with enhancement of oxidation protection improved the dimensional stability. Thermocycling tests showed that the number of cycles to failure depends on the amount of Al alloying and the applied high-temperature exposure during each cycle. SEM/EDX, high-resolution TEM and mu CT analysis were used to verify the mechanism resulting from the Al alloying protection. It was shown that an optimal level of Al alloying for balancing oxidation and thermal cracking resistance depends on thermomechanical conditions of application.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据