期刊
IEEE SENSORS JOURNAL
卷 22, 期 4, 页码 3017-3023出版社
IEEE-INST ELECTRICAL ELECTRONICS ENGINEERS INC
DOI: 10.1109/JSEN.2021.3139168
关键词
Sensors; Lead; Temperature sensors; Surface treatment; Gas detectors; Adsorption; Temperature measurement; Gas sensor; colloidal quantum dot; lead sulfide; size-engineering; nitrogen oxide
资金
- National Natural Science Foundation of China [61861136004, 62004100]
- Program for HUST Academic Frontier Youth Team [2018QYTD06]
- Innovation Fund of WNLO
Colloidal quantum dots (CQDs) with large surface-to-volume ratio and highly reactive surfaces, combined with solution-processability, hold promise as the next generation gas-sensing materials. In this study, controllable synthesis of PbS CQDs with diameter sizes ranging from 2.7-7.0 nm was achieved by adjusting the injection temperature, precursor concentration, and cooling rate. The results showed that cold bath cooling method exposed more {100} facets and enhanced NO2-sensing properties at room temperature. The study also revealed the microstructural mechanism underlying the size engineering of CQDs-based gas sensors.
The large surface-to-volume ratio and highly reactive surfaces, combined with solution-processability make colloidal quantum dots (CQDs) promising to be the next generation of gas-sensing materials. However, the size- engineering gas-sensing behavior of CQDs has not been further studied. Herein, we report the controllable synthesis of PbS CQDs with diameter sizes ranging from 2.7-7.0 nm through adjusting the injection temperature, precursor concentration and cooling rate. The results showed that the method of cold bath cooling exposed more {100} facets and enhanced NO2-sensing properties at room temperature. According to the first principle calculation, the {100} facets of PbS CQDs favors the competitive adsorption of NO2 with O-2 molecules, which is in contrast with the {111} facets. At the same time, rapid cooling rate helps to increase the density of intra-band trap states of PbS CQDs, which may favor the interdot carrier hopping so as to transduce the charge transfer during the competitive adsorption between NO2 and O-2 molecules into enhanced electrical current. This work reveals the microstructural mechanism underlying the size engineering of CQDs-based gas sensors.