Tailoring of a highly stable Mn1-x-y(CexLay)O2-δ pseudocapacitor thin-film and rare earth oxide nanospheres through selective purification of rare earth oxides derived from Ni-MH batteries

Growing utilisation of rare earth elements (REEs) has caused severe shortages in REE supply and shifted the state-of-the-art approaches toward sustainable recycling of REEs containing wastes. The present work reports a three-step strategy based on selective purification of rare earth oxides (REOs) isolated from end-of-life nickel-metal hydride (Ni-MH) batteries leading to a high-yield fabrication of two value-added functional nanostructures including a defect-rich Mn1-x-y(CexLay)O2-delta film and REO nanospheres. During the first step, major impurities (Fe and Al) were removed from a REE-rich solution. In step two, the resulting solution with a trace amount of Mn was further purified through electrodeposition resulting in the synthesis of a non-stoichiometric Mn1-x-y(CexLay)O2-delta film, in which Ce4+/3+ and La3+ ions were dissolved in an MnO2-x lattice. The pseudocapacitance functionality of the film showed a high volumetric capacitance of 828 F cm(-3) with an outstanding retention of 83% after 16 000 cycles. The excellent electrochemical performance was attributed to an improved charge carrier transfer rate, a significant number of active sites, and an intervalence charge transfer (IVCT) phenomenon occurring between Mn and Ce cations with multiple oxidation states. Furthermore, a symmetric solid-state two-electrode device validated the practical functionality of the film. During the last step, the remaining solution was purified further that led to the formation of REO (La, Ce, and Nd) nanospheres with similar to 40-50 nm diameter. Lastly, a brief comparative environmental impact analysis was conducted, revealing the remarkable ecological importance of such waste valorisation process.

Automated summary

This study presents a three-step strategy for the high-yield fabrication of two value-added functional nanostructures through selective purification of REOs isolated from end-of-life Ni-MH batteries. The study also demonstrates the remarkable electrochemical performance and practical functionality of the fabricated nanostructures.