Study of the effects of rabbit scleral fibroblasts on cellular biomechanical properties and MMP-2 expression using two modes of riboflavin/ultraviolet A wave collagen cross-linking

Objective: The aim of this study is to evaluate the cellular biomechanical properties and MMP-2 expression changes in rabbit scleral fibroblasts using two modes of riboflavin and ultraviolet A (UVA) collagen cross-linking (CXL). Methods: Twenty-four New Zealand white rabbits were randomly divided into two groups, A and B. The left eye was chosen for the experimental group and the right eye for the control group. In group A, the eyes were irradiated for 30 min, with a power density of 3.0 mW/cm2. In group B, the eyes were irradiated for 9 min, with a power density of 10.0 mW/cm2. One week after CXL, full-field electroretinography was performed. Sixty days after CXL, the rabbits were sacrificed, and scleral fibroblasts were extracted from the CXL-treated sclera area and corresponding parts of control sclera and cultured. Cellular biomechanical properties were evaluated using the micropipette aspiration technique, and the MMP-2 protein expression was determined by Western blot analysis. Results: There was no statistical difference in the amplitude and latency of the dark adaptation 3.0 and light adaptation 3.0 between the CXL and control eyes of groups A and B (P > 0.05). Compared with the control groups, the Young's modulus of the fibroblasts and apparent viscosity of the experimental eyes in groups A and B were increased after CXL (P < 0.05), but there was no significant difference between the two groups under different irradiation modes (P > 0.05). The MMP-2 expression in scleral fibroblasts from experimental eyes was significantly higher than that in scleral fibroblasts from control eyes in groups A and B. Under the two different irradiation modes, the MMP-2 expression in the scleral fibroblasts from experimental eyes in group A was significantly higher than that in the scleral fibroblasts from experimental eyes in group B. Conclusion: The riboflavin-UVA scleral CXL conducted in two different modes produced no significant side effects on the retina and could strengthen the cell biomechanical properties as well as increase the MMP-2 expression of scleral fibroblasts significantly.

Automated summary

This study evaluated the cellular biomechanical properties and MMP-2 expression changes in rabbit scleral fibroblasts using two different modes of riboflavin and ultraviolet A collagen cross-linking. The results showed that both modes of cross-linking did not have significant side effects on the retina, but they significantly enhanced the cell biomechanical properties and increased MMP-2 expression in scleral fibroblasts.