Unforeseen, negative interaction-effect of adjacent circumferential notches on the fatigue limit of Ni-based superalloy 718

期刊

ENGINEERING FRACTURE MECHANICS
卷 257, 期 -, 页码 -

出版社

PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.engfracmech.2021.108015

关键词

Ni-based superalloys; Fatigue limit; Circumferential notch; Stress-field interaction; Shear-mode crack

向作者/读者索取更多资源

The study investigated the interaction-effects of adjacent, circumferential V-notches on the fatigue limit of Alloy 718, and found that specimens with seven adjacent circumferential notches had lower fatigue limit than those with a single circumferential notch. This was attributed to the increased stress intensity factor range of shear-mode fatigue cracks at notch-roots, resulting from the competition between stress mitigation through the mechanistic interaction of notches and the orderly spatial alignment of crack-planes.
Investigations were conducted on the interaction-effects of adjacent, circumferential V-notches on the fatigue limit of Alloy 718, with the aid of fully-reversed, tension-compression fatigue tests. Contrary to expectation, specimen with seven adjacent circumferential notches had lower fatigue limit than that with a single circumferential notch. This phenomenon was attributed to the increased stress intensity factor (SIF) range of shear-mode fatigue cracks at notch-roots, resulting from competition between two factors: (i) stress mitigation through the mechanistic interaction of notches (decreased SIF) and (ii) the orderly, spatial alignment of crack-planes, due to the asymmetric stress-fields in the vicinity of notch-roots (increased SIF).