A Non-isocyanate Route to Poly(ester urethane) with High Molecular Weight: Synthesis and Effect of Chemical Structures of Polyester-diol

A series of non-isocyanate linear high molecular weight poly(ester urethane)s (PETUs) were prepared through an environmentally-friendly route based on dimethyl carbonate, 1,6-hexanediol and 1,6-hexanediamine. In this route, the polyurethane diol was first prepared by the reaction between bis-1,6-hexamethylencarbamate (BHC) and 1,6-hexanediol. A series of polyester soft segments of polyurethane have been synthesized from the polycondensation of adipic acid and different diols, including butanediol, hexanediol, octanediol and decanediol. The subsequent polycondensation of polyurethane diol and polyester diol led to linear PETUs. The resultant polymers were characterized by GPC, FTIR, H-1-NMR, C-13-NMR, DSC, WAXD, TGA and tensile test. The results indicated that PETUs possess weight-average molecular weights higher than 1x10(5) and the tensile strength as high as 10 MPa. The thermal properties, crystallization behavior, microphase separation behavior and morphology were studied by DSC and AFM, and the results indicated that the degree of phase separation was affected by two factors, the crystallization and hydrogen bonding interaction between soft segment and hard segment.

Automated summary

A series of non-isocyanate linear high molecular weight poly(ester urethane)s (PETUs) were prepared through an environmentally-friendly route, and their properties were characterized. The results showed that PETUs have high molecular weights and tensile strength, with the degree of phase separation being affected by crystallization and hydrogen bonding interaction.