Raman identification of the different glazing technologies of Blue-and-White Ming porcelains

Shards of Blue-and-White Ming porcelain from shipwrecks of Portuguese ships found on the coasts of South Africa plus a shard from Mombasa (Kenya) were analyzed by optical microscopy, SEM-EDS and Raman microspectroscopy (458 nm). Whereas the Raman signature of porcelain body paste compositions which are based on mullite, quartz and an amorphous phase with the minor presence of anatase and feldspar are very comparable whatever the variable alumina content, at least two types of glazes are observed: a high-temperature soda-potassium glaze, and glazes richer in calcium and similar to a celadon glaze (with the possibility of wollastonite formation). The blue decoration is obtained with a material rich in manganese typical of the Ming productions. Some shards exhibit a two-layer glaze and the blue decoration is either placed under-glaze, or in-glaze as found in the Vietnamese productions of the same period. Previous assignments of the Raman signature of feldspar to cobalt aluminate are now not favoured (blue colour is obtained with Co2+ ions dissolved in the glassy silicate) and several black spots exhibit the characteristic spectrum of an epsilon Fe2O3 phase being present.

Automated summary

Shards of Blue-and-White Ming porcelain from shipwrecks of Portuguese ships found on the coasts of South Africa, as well as a shard from Mombasa (Kenya), were analyzed using optical microscopy, SEM-EDS, and Raman microspectroscopy. The study revealed differences in the composition of the porcelain body paste and types of glazes used, with blue decoration characteristic of materials rich in manganese.