Preparation and corrosion resistance of a self-sealing hydroxyapatite- MgO coating on magnesium alloy by microarc oxidation

An ideal self-sealing hydroxyapatite (HA)-MgO coating was designed on an AZ31 Mg alloy by one-step microarc oxidation (MAO) with the addition of HA nanoparticles into a base electrolyte. The formation mechanism of the self-sealing HA-MAO coating was discussed. The effect of the nano-HA addition on the corrosion resistance of the MAO coating was evaluated by corrosion tests in Hank's solution. The results show that HA nanoparticles inertly incorporated into the MAO coating during the process of coating growth. HA and MgO were the main constituents of the HA-MAO coating. The HA nanoparticles were absent in the inner barrier layer but concentrated in the outer porous layer. In addition, HA nanoparticles accumulated much more inside coating defects than in the other zones, which resulted in the nearly ideal sealing of micropores on the coating surface. By forming a denser and more stable outer layer, the incorporation of HA nanoparticles greatly enhanced the anti-corrosion properties of the MAO coating.

Automated summary

By incorporating HA nanoparticles into the base electrolyte during the one-step microarc oxidation process, an ideal self-sealing HA-MAO coating was successfully designed. The HA nanoparticles inertly incorporated into the coating, resulting in nearly ideal sealing of micropores on the coating surface. In addition, the addition of HA nanoparticles greatly enhanced the corrosion resistance properties of the coating.