Silicon nitride; Selective laser sintering; Cold isostatic pressing; Bending strength; Antenna window
资金
- National Natural Science Foundation of China [50872108]
By adding sintering aids and utilizing the CIP process, the bending strength of Si3N4 ceramics can be significantly enhanced, resulting in the optimal performance of the ceramics.
In this study, a high-strength silicon nitride (Si3N4) antenna window was successfully developed via selective laser sintering (SLS) with cold isostatic pressing (CIP) after debinding before final sintering. The effects of CIP after debinding and sintering additives on the bulk density, total porosity, bending strength and microstructure of Si3N4 ceramics were examined. The results show that the bending strength of SLS Si3N4 ceramics can be greatly improved by adding sintering aids between Si3N4 granules and by CIP after debinding. Optimal performance of ceramics is obtained by CIP after debinding and the use of inter-granule sintering additives. The porosity, bulk density, and bending strength are 18.7%, 3.11 g/cm(3), and 685 MPa, respectively. Eliminating the pores by the CIP after debinding and by inter-granule sintering additives promotes the growth of rod-like beta-Si3N4, which lock with each other contribute to the strengthening of Si3N4 ceramics.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据