The role of polarization in the threshold voltage of field effect transistors based on ZnO/MgO

期刊

APPLIED PHYSICS LETTERS
卷 119, 期 16, 页码 -

出版社

AIP Publishing
DOI: 10.1063/5.0065968

关键词

-

资金

  1. SCAIT [E653CX]
  2. CONICET [PIP 585, PICT 2016-3356]

向作者/读者索取更多资源

The work reported on the fabrication and characterization of a field effect transistor based on a ZnO/MgO bilayer with a top-gate configuration. X-ray diffraction patterns showed epitaxial growth of ZnO and MgO films. The intrinsic properties of transparent conducting oxides were shown to determine key parameters of a FET device.
In this work, we report on fabrication and characterization of a field effect transistor (FET) based on a ZnO/MgO bilayer employing a top-gate configuration. X-ray diffraction patterns show that the resulting ZnO and MgO films grow epitaxially with planes (002) and (111) parallel to the substrate surface, respectively. Typical current-voltage curves for different applied gate voltages are obtained, and the results are well fitted using standard FET equations. From these fittings, an extracted electronic mobility of mu = 0.8 cm(2)/V s was obtained in close agreement with the value extracted from Hall effect measurements. A threshold voltage of V T H = - 34 & PLUSMN; 3 V was obtained, which is the value that can be explained by the polarization difference of both materials. UV illumination shifts the V-TH to V T H = - 43 & PLUSMN; 1 V. These findings show how the intrinsic properties of transparent conducting oxides can determine key parameters of a FET device.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.6
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据