Delamination and Engineered Interlayers of Ti3C2 MXenes using Phosphorous Vapor toward Flame-Retardant Epoxy Nanocomposites

As recently created inorganic nanosheet materials, more and more light has been shed on MXenes, which have emerged as a hotspot of intensive investigations. The simple exfoliation method for MXenes attracts numerous studies to pay efforts on. Compared with the extensive research about ultrasonication and mechanical milling, gasassisted exfoliation has never been carried out for MXenes. Meanwhile, MXene-based nanocomposites are always prepared after exfoliation step by step. In this work, a facile way to fabricate a few-layered Ti3C2 MXene delaminated using phosphorous vapor evolved from commercial red phosphorous (RP) is put forward. The vapor deposits on the surface of Ti3C2 and also partially intercalates into the interlayers to obtain a novel two-dimensional RP/Ti3C2 nanocomposite directly. The P element strongly connects with the substrate by a covalent bond that improves the safety problems for RP during storage and usage. Due to the versatile feature of MXenes, the nanocomposite has the potential to be applied in a variety of fields. Herein, it is employed as a flame retardant for epoxide resin and effectively reduces fire disaster. The one-step exfoliation plus nanocomposite fabrication provides a more feasible way for the practical application of MXenes.

Automated summary

This study introduces a simple method of delaminating Ti3C2 MXene using phosphorous vapor to obtain a two-dimensional RP/Ti3C2 nanocomposite. The method improves the safety issues of red phosphorous during storage and usage, while the MXene nanocomposite shows versatile potential applications in various fields.