HYDROMETALLURGY
卷 159, 期 -, 页码 1-5出版社
ELSEVIER
DOI: 10.1016/j.hydromet.2015.09.019
关键词
Vanadium; Vanadium slag; Leaching; Electro-oxidation
资金
- Chongqing University Postgraduates' Innovation Project
- National Key Basic Research and Development Program [2011CB933300]
- National Science Foundation of China [51074200]
An improved process for the leaching of vanadium from vanadium slag assisted by electro-oxidation was developed to increase the leaching ratio of vanadium. Factors associated with the leaching process were investigated, and a high vanadium leaching ratio (>70%) was achieved under the optimal leaching condition of 40 wt.% H2SO4, 250 g/L solid concentration, anode current of 0.4 A, operating potential of 2.8-3.0 V, and electrode spacing of 20 mm at 75 degrees C for 4 h. X-ray diffraction patterns showed that the spinels and silicate were the major phases in the vanadium slag, and vanadium was in the form of FeV2O4 (namely of FeO center dot V2O3). Scanning electron microscopy studies indicated that the spinels were broken into small pieces and vanadium was exposed on the surface, leading to facile oxidation and high vanadium leaching ratio, and demonstrated that electro-oxidation could significantly enhance the leaching process. (C) 2015 Published by Elsevier B.V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据