HYDROMETALLURGY
卷 164, 期 -, 页码 90-96出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.hydromet.2016.05.013
关键词
Uranium; Phosphoric acid; Solid phase extraction; D2EHPA-TOPO/SiO2-P
This paper describes uranium extraction from aqueous phosphoric acid medium using a silica/polymer based D2EHPA-TOPO adsorbent. The mixture of di-2-ethyl-hexylphosphoric acid (D2EHPA) and tri-n-octylphosphine oxide (TOPO) was impregnated and immobilized into the pores of SiO2-P particles. The various experimental parameters such as the synergistic mixture ratio of extractants, phosphoric acid concentration, the contact time and the temperature were investigated. The results showed that 95% uranium extraction was achieved after 10 min contacting time using D2EHPA-TOPO/SiO2-P (mass ratio = 3:1 w/w) adsorbent from 1 M phosphoric acid solution containing 165 ppm U (VI), 5000 ppm Fe (III), 1000 ppm Ca (II) and 1000 ppm Al(Ill) at 25 degrees C. Also, the obtained results displayed the high adsorption capacity for Uranium as high as 48 mg g(-1) at the mentioned conditions. The rate constant (1.62 g mg(-1) min(-1)) was calculated by the pseudo-second order equation and it shows that reaction rate was controlled by the chemical adsorption of uranium. Furthermore, D2EHPA-TOPO (3:1)/SiO2-P has a good selectivity for U(VI) among the co-existing elements (Fe, Al and Ca). The adsorption isotherms were well described by the Redlich-Peterson equation, closely followed by the Langmuir equation which confirms the mechanism is chemical monolayer adsorption. Obtained thermodynamic parameters (Delta H degrees.Delta S degrees and Delta G degrees) reveal that the U(VI) adsorption to be an exothermic and spontaneous process. (C) 2016 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据