HEAT TREATMENT EFFECT ON MARAGING STEEL MANUFACTURED BY LASER POWDER BED FUSION TECHNOLOGY: MICROSTRUCTURE AND MECHANICAL PROPERTIES

Laser Powder Bed Fusion (L-PBF) is a widespread additive manufacturing technology in industrial applications, for metal components manufacturing. Maraging steel is a special class of Fe-Ni alloys, typically used in the aerospace and tooling sectors due to their good combination of mechanical strength and toughness. This work analyses the heat treatment effect on the microstructure and hardness value of 300-grade maraging steel manufactured by the L-PBF process. The considered heat treatment consists of a solution annealing treatment followed by quenching and ageing hardening treatment. The effect of ageing temperature is reported, in a wide temperature range. Results show that solution annealing treatment fully dissolves the solidification structure caused by the L- PBF process. Moreover, the ageing hardening treatment has a significant impact on the hardness, hence on strength, of L-PBF maraging steel. The optimal ageing conditions for the L-PBF maraging steel are identified and reported: in particular, results show that the hardness of 583 HV is achieved following ageing treatment at 490 degrees C for 6 hours. A higher treatment temperature leads to over-ageing resulting in a decrease of hardness. Conversely, an excessive ageing time does not seem to affect the hardness value, for the ageing temperature of 490 degrees C.

Automated summary

This research analyzed the heat treatment effect on 300-grade maraging steel manufactured by L-PBF process, identifying the optimal ageing conditions and the significant impact of ageing hardening treatment on hardness and strength.