On the role of boron, carbon and zirconium on hot cracking and creep resistance of an additively manufactured polycrystalline superalloy

期刊

MATERIALIA
卷 19, 期 -, 页码 -

出版社

ELSEVIER SCI LTD
DOI: 10.1016/j.mtla.2021.101193

关键词

Additive manufacturing; Ni-based superalloys; Hot cracking; Creep; Grain boundary segregation

向作者/读者索取更多资源

The study investigates the relationship between hot cracking susceptibility and creep resistance in a nickel-based superalloy with different contents of boron, carbon and zirconium. By analyzing the distribution of these elements at grain boundaries, the research reveals the importance of alloy design guidelines for achieving both crack-free fabrication and required creep performance after heat-treatment. The presence or absence of specific elements at grain boundaries plays a crucial role in determining the alloy's properties.
We investigate the hot cracking susceptibility and creep resistance of a nickel-based superalloy with three different contents of boron, carbon and zirconium fabricated by laser powder bed fusion. Crack-free and creep resistant components are achieved for the alloy version with boron, carbon and no zirconium. We then rationalize this result by evaluating how boron, carbon and zirconium are distributed at grain boundaries in the as-built and heat-treated microstructures of an alloy containing all these elements. Observations are conducted by scanning and transmission electron microscopy, and atom probe tomography. In the as-built microstructure, boron, carbon and zirconium segregate at high-angle grain boundaries as a result of solute partitioning to the liquid and limited solid-state diffusion during solidification and cooling. After heat-treatment, the amount of boron and carbon segregating at grain boundaries increases significantly. In contrast, zirconium is not found at grain boundaries but it partitions at the gamma' precipitates formed during the heat treatment. The presence of zirconium at grain boundaries in the as-built condition is known to be susceptible to enhance hot cracking, while its absence in the heat-treated microstructure strongly suggests that this element has no major effect on the creep resistance. Based on our observations, we propose alloy design guidelines to at the same time avoid hot cracking during fabrication and achieve the required creep performance after heat-treatment.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.1
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据