Tungsten; Amorphous alloy; Wetting; Joining; Interface diffusion
资金
- Central University , JLU
- Jilin Province Science and Technology plan [20170204026GX]
Cu-Ti based amorphous fillers were designed to facilitate the joining of tungsten heavy alloy (WHA) and Fe-Ni-Co based superalloy (GH907), resulting in superior wettability and strength. Typical microstructures of brazed joints were identified, with a maximum joint shear strength of 340 MPa achieved at 1050 degrees C for 10 minutes, highlighting effective joining mechanisms involving diffusion-reaction behavior and dissolution-dilution effect.
Cu-Ti based amorphous fillers were designed based on cluster-plus-glue-atom model to join tungsten heavy alloy (WHA) and Fe-Ni-Co based superalloy (GH907). The wettability of WHA by brazing fillers was analyzed, and the interfacial microstructures and mechanical properties of brazed joints were also investigated. High constituent homogeneity and excellent flowability of amorphous fillers facilitated the superior wettability and brazeability effectively. In addition, WHA substrate/ beta - Ti /(Cu, Ni)(Ti, Zr) + (Cu, Ni)(Ti, Zr)(2) /(Fe, Ni)Ti + Fe2Ti/GH907 substrate were identified as typical microstructures of brazed joints, and the maximum joint shear strength of 340 MPa was obtained at 1050 degrees C for 10 min. The underlying joining mechanisms were addressed in view of diffusion-reaction behavior and dissolution-dilution effect of multiple alloying elements.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据