Properties of Polyethylene Terephthalate (PET) after Thermo-Oxidative Aging

The influence of the thermo-oxidative aging semi-crystalline polyethylene terephthalate process on the thermal and mechanical properties was analysed in the article. For this purpose, PET was aged at 140 degrees C for 21, 35 and 56 days. The research showed that as a result of aging, the amount of the crystalline phase increases by about 8%, which translates into the properties of the aged material. The glass transition and melt temperature of lamellar crystals formed during first and second crystallisation increase with aging. The mechanical properties of the material were analysed in the temperature range of 25 to 75 degrees C. The tests were showing an increase in Young's modulus and a decrease in elongation at the break as a result of aging. This phenomenon was particularly visible during tests at 75 degrees C and during the morphological observation of the fracture surface, where the fracture character of the material changes from ductile to brittle. In the case of the material aged for the longest time, the temperature has a negligible influence on the elongation at break.

Automated summary

The influence of thermo-oxidative aging on semi-crystalline polyethylene terephthalate was analyzed in the article, showing an increase in crystalline phase content and crystalline temperature with aging, as well as an increase in Young's modulus and decrease in elongation at the break.